California failure analysis lab is able to show similarities between glass failure analysis and porcelain failure analysis. The predominant tool for tracking a crack in glass is to look at “Wallner lines” These can tell the direction of travel of a crack in glass. This allows the glass failure expert to trace the crack back […]
Read Consulting Failure Analysis Blog
In addition, READ CONSULTING provides services to industry in the areas of failure analysis, process development and process improvement. Read Consulting is prepared to use its experience and expertise to analyze customers' specific problems.
Failure Analysis Lab Examines a Failed Plastic Chair
California failure analysis laboratory performed a failure analysis on a failed plastic chair. A 190 pound man sat in it and the right leg broke under him. This was a brittle plastic failure that went along a molding weld line. The fracture surface shows brittle failure in bending.
Glass Expert Discusses Bend Test Fracture Surface
California Failure Analysis lab performed a compound bend test to determine if the failure surface can be at an angle to the surface. One curious result was a curved fracture surface. This occurs when the clamp on the topside (i.e. tensile side) was behind the support underneath. If the two clamped sides are aligned, the crack is […]
Glass Expert Performs Glass Bottle Failure Analysis
Read Consulting failure analysis lab was asked to determine the cause of failure of a small glass cosmetic bottle that had failed in on the filling line as the cap was being tightened. A glass failure analysis was performed using a low power microscope. The root cause of the failure was a chill check on […]
Glass Expert Discusses Modern Auto Windshields
California glass expert has been involved with evaluation automobile windshields. One way car manufacturers can increase automobile mileage is to decrease weight. A part of this effort has been to reduce the weight of automobile windshields. This is done by reducing the thickness of the windshield. Upper left is a representative cross section of a […]