California glass expert performs a failure analysis on a wine bottle failure. In this case the root cause of the failure was due to an impact on the top of the bottle finish. it is apparent that this bottle was hit on the top. This is shown by the photomicrograph.
Glass Failure Analysis Of Bottle Defect
California Glass Expert Witness was assigned to determine the cause of failure of wine bottles at the manufacturing facility. During processing the bottles had a higher than normal failure rate. A root cause failure analysis was performed by the glass failure analysis expert witness. He inspected a large number of whole bottles and removed those […]
Manufacturing Defect on Tempered Glass Window
Glass failure analysis expert witness performed a root cause failure analysis on window defects found on a recently built custom home. The upper left photograph shows the defect from the building exterior. The window defect resembles a dust or dirt streak and was not detected until the post construction window cleaning. In all cases, the […]
Tempered Glass Expert Describes Two Tempered Glass Fracture Surfaces
Glass failure analysis expert witness compares two typical tempered glass fractures. The lower photomicrograph shows a typical thermally tempered glass fracture surface . This piece is from a fully tempered glass sheet. That is; this glass has a surface compression stress of 10,000 psi or more. In addition, the compressive layer on each face is […]
Product Liability, Chair Failure Analysis
Failure analysis expert witness examined a failed hospital chair. The chair failed during a breast X-ray examination. The chair had been altered 3 years prior to the failure, and the machine shop that had made the alterations was accused of causing the fatigue failure. Examination of the chair discovered hammer marks on a critical region […]