Glass Expert Performs Failure Analysis on Glass Blender Jar

April 19, 2013 By Tom Read Leave a Comment

The glass experts at Read Consulting in Santa Rosa California performed a glass failure analysis on a borosilicate glass blender jar that failed in a glass thermal shock test as a part of product qualification. The jar is operated with a stainless steel spoon inside. It is then subjected to thermal shock test by heating […]

Filed Under: Failure Analysis Tagged With: Borosilicate Glass, Glass Blender, Jar, Thermal Shock

Coffee Pot Failure Analysis

August 12, 2011 By Tom Read Leave a Comment

A failure analysis was performed on a glass coffee press. In this case the glass coffee pot is a 0.085″ thick borosilicate glass 3.7″ diameter cylinder that is 7″ high. It had received a blow on the top rim, and it broke into approximately 10 pieces. Because the pot is a cylinder, the blow from […]

Filed Under: Failure Analysis Tagged With: Borosilicate Glass, Coffee Pot

Failure Analysis: “Exploding” Coffee Pot

July 25, 2011 By Tom Read Leave a Comment

California failure analysis expert was presented with the claim that a coffee pot had “exploded” when replaced on the coffee warmer in a convenience store.First of all, there is no “stored” energy to cause an explosion. The coffee is not under pressure, and the pot is made from annealed borosilicate glass. In addition, the broken […]

Filed Under: Failure Analysis Tagged With: Borosilicate Glass, Coffee Pot, Exploding, Glass

Plumbing Failure Analysis: Failure Analysis of a Water Flow Indicator

July 20, 2011 By Tom Read Leave a Comment

A California failure analysis expert performs a failure analysis on a broken water flow indicator. This flow indicator was in a large building, and as a result of the failure, there was substantial damage. The flow indicator consisted of a glass dome clamped into a metal housing.The failure originated where the flange of the glass […]

Filed Under: Failure Analysis Tagged With: Borosilicate Glass, Glass, Water Flow Indicator

Pyrex Glass Failure Analysis: Glass Baking Dish Failure Analysis

July 12, 2010 By Tom Read Leave a Comment

California glass expert witness performed a failure analysis on a pyrex glass baking dish. This dish was made from pyrex borosilicate glass, and the glass failure occured as the dish was being removed from the oven. The failure initiated at an internal glass defect. The defect appears to be a colapsed bubble (seed) in the […]

Filed Under: Failure Analysis Tagged With: Borosilicate Glass, Glass, Pyrex, Tempered Glass

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering