Glass failure analysis expert locates the origin of a failed wine bottle. Thye failure origin is at the top of the bottle on the inside rim. The origin is a crush spot on the inner rim. This was too high to be caused by a corkscrew. It is believed that the damage occurred […]
Glass Damage from Weld Spatter
At a new condominium complex, numerous windows were discovered to have been damaged by weld spatter. Upper left is a photograph of typical damage found on the affected windows. A glass expert examined the damage to determine if the windows could be repaired. A glass failure analysis was performed to evaluate the damage level. Microscopic […]
Glass Expert Performs Sauce Bottle Glass Failure Analysis
Glass expert peformed a bottle failure analysis on a broken bottle of steak sauce . Intitally it was stated that this was a new and unopened bottle; however, examination revealed that there was sauce on the bottle threads. In addition, the “band” below the plastic lid was not connected. From this it was concluded that […]
Failure Analysis Expert Discusses Metal Fatigue
Failure analysis was performed on a failed pin from a large tractor. The upper right gives an overview of the pin. Upper left is a close up of the fracture surface. The fatigue crack originated at the top of the photo and progressed downward until the final overload failure.
GLass Expert Analyzes Wine Bottle Failure
Glass expert analyzed several leaking wine bottles that eventually broke in half. All the bottle failures occured on the heal. Also, during failure analysis, it was discovered that all of the bottle failures were made in one cavity of a multi-cavity bow mold tool. Bottles from the other cavities did not have this problem. These […]