Glass Expert Examines a Tempered Glass Window Failure

March 19, 2011 By Tom Read Leave a Comment

California failure analysis expert uses glass fractography to perform a glass failure analysis on a tempered glass window failure. The glass fracture analysis showed that the window failure was a result of heating the glass in the center. Due to the heat, the center of the window expanded. This created additional tensile stress on the […]

Filed Under: Failure Analysis Tagged With: Expert Witness, Glass, Tempered Glass, Thermal Stress

California Glass Expert Performs a Failure Analysis on a Glass Bowl

February 25, 2011 By Tom Read Leave a Comment

A glass failure analysis was performed on a glass mixing bowl. An overview of the failed glass bowl is shown in the upper left photograph. This bowl failed as a result of thermal stresses. The crack originated at the bottom of the bowl and spread in one direction around the entire bottom. The thermal stresses […]

Filed Under: Failure Analysis Tagged With: Fracture, Glass Bowl, Mixing Bowl, Thermal Stress

Failure Analysis Expert Examines a Plumbing Failure

February 14, 2011 By Tom Read Leave a Comment

A failure analysis was performed on a plumbing failure. The line is a corrugated water line to a bathroom sink. The pipe failure occurred at a bend in the water supply line it was due to stress corrosion of the yellow brass line. Microscopic examination of the largest crack showed that there was also dezincification […]

Filed Under: Failure Analysis Tagged With: Brass Tubing, Corrugated Water Line, mechanical deformation, Plumbing

Failure Analysis of Broken Tempered Glass Window

January 24, 2011 By Tom Read Leave a Comment

Failure analysis of tempered glass windows is normally impossible because the failed window falls apart into a large number of similar pieces, and locating the origin is impossible. However, there are cases when the window remains intact, and root cause failure analysis is possible. In this case the glass expert was able to preserve the […]

Filed Under: Failure Analysis Tagged With: Nickel Sulfide, NiS particle, Photomicrograph, Tempered Glass, Window

Failure Analysis Expert Examines a Corrosion Failure

January 17, 2011 By Tom Read Leave a Comment

Corrosion engineer performed a metallurgy failure analysis to determine the cause of prematurely failing burners in a particular brand of gas grill. The burners in question would fail completely after two or three years of service. The failure analysis of the burner revealed that the grill manufacturer made the subject gas burners from an inferior […]

Filed Under: Failure Analysis Tagged With: Burners, Corrosion Failure, Gas Grill, Stainless Steel

  • « Previous Page
  • 1
  • …
  • 37
  • 38
  • 39
  • 40
  • 41
  • …
  • 61
  • Next Page »

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering