Failure Analysis of Glass Pot: Visions Cookware

October 5, 2011 By Tom Read Leave a Comment

A failure analysis  was performed on a broken 5 quart stove top glass pot. The origin was determined with optical microscopy, and the broken pot was assembled to show how cracking proceeded. The re-assembled pot is shown upside down in the upper left photograph. The failure originated at a preexisting “chip” on the interior at […]

Filed Under: Failure Analysis Tagged With: Cookware, Glass, Manufacturing Defect, Tempered Glass

Rubber Failure Analysis Demonstrates Rubber Fatigue

September 27, 2011 By Tom Read Leave a Comment

California rubber failure analysis expert performs a failure analysis on a rubber paddle. This piece failed as a result of fatigue. The fatigue failure initiated on the outer surface at a stress riser and progressed inwards. This is demonstrated by the photomicrographs above. Upper left is taken at 10X. Upper right is taken at 40X. […]

Filed Under: Failure Analysis Tagged With: Fatigue, Photomicrograph, Rubber Failure

Medical Device Failure Analysis of a Catheter

September 20, 2011 By Tom Read Leave a Comment

California failure analysis expert witness performed a failure analysis on a piece of rubber that had been removed from a patient’s bladder. The piece was compared with the tip of a new exemplar catheter. Although the piece that was removed surgically was encrusted with salts, it was shown to be part of a catheter.

Filed Under: Failure Analysis Tagged With: Catheter, Medical Device, Rubber

Swing Set Failure Analysis

September 11, 2011 By Tom Read Leave a Comment

California failure analysis expert analyzes forces necessary to cause a swing set to fail. There are times that it is claimed that a swing set failed under “normal use” conditions. Tests were performed to determine what minimum forces are necessary to cause the chain to be pulled from the ‘S’ hook that holds it to […]

Filed Under: Failure Analysis Tagged With: Metal, Swing Set

Failure Analysis: Hurricane Window Defects

August 29, 2011 By Tom Read 2 Comments

Laminated Glass: A glass failure analysis expert witness was engaged to inspect hurricane window defects. These windows were sold to meet the Miami Dade/State of FloridaBuilding Code Requirements for hurricane resistance, and during development of the process, it appears as if these requirements were met. However, the laminating plastic in these windows interacted with the […]

Filed Under: Failure Analysis Tagged With: Hurricane Window, Laminated Window

  • « Previous Page
  • 1
  • …
  • 33
  • 34
  • 35
  • 36
  • 37
  • …
  • 61
  • Next Page »

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering