Plastic Pipe Expert Performs Failure Analysis on Failed PVC Pipe Elbow

October 8, 2013 By Tom Read Leave a Comment

The PVC pipe expert at Read Consulting was asked to perform a failure analysis of a failed PVC “glue joint” elbow that had failed in service and that had caused a significant amount of water damage. The failed PVC pipe elbow was submitted for failure analysis. Upper left is the as received elbow with a […]

Filed Under: Failure Analysis Tagged With: Failed PVC, Plastic Pipe, PVC Pipe Elbow

Metallurgical Failure Analysis: Failed Cast Steel Pipe

August 27, 2013 By Tom Read Leave a Comment

  Metallurgists at Read Consulting were asked to perform a metallurgical failure analysis of a cast steel pipe that had burst. The pipe was in a high pressure concrete delivery system that was pumping concrete to a top floor of a parking garage. The pipe burst unexpectedly, and a worker was injured. A part of […]

Filed Under: Failure Analysis Tagged With: Failed Cast Steel Pipe, Metal, Steel Pipe

California Glass Expert Performs a Failure Analysis of Sparkling Liquor Bottle Failures

July 19, 2013 By Tom Read Leave a Comment

A bottling line for sparkling drinks was suffering from a high rate of  bottle failures on the bottling line. In addition, several bottles failed on the shelf after bottling. Read Consulting was asked to perform a glass failure analysis to determine the cause of failure of three bottles that had failed “on the shelf”. Two […]

Filed Under: Failure Analysis Tagged With: Glass Bottle, Liquor Bottle.Glass, Manufacturing Defect

Steel Tank Failure: Metal Failure Analysis of a Collapsed Bolted Steel Holding Tank

May 28, 2013 By Tom Read Leave a Comment

 Read Consulting was contracted to perform a root cause failure analysis on a collapsed 40,000 gallon water holding tank. Metal corrosion is the root cause of the tank failure. The failure originated at the bottom of the tank on the West side. The initial failure resulted from corrosion on bolts holding the side of the […]

Filed Under: Failure Analysis Tagged With: Collapsed Bolted Steel, Holding Tank, Metal, Steel, Tank Failure

Glass Expert Performs Failure Analysis on Glass Blender Jar

April 19, 2013 By Tom Read Leave a Comment

The glass experts at Read Consulting in Santa Rosa California performed a glass failure analysis on a borosilicate glass blender jar that failed in a glass thermal shock test as a part of product qualification. The jar is operated with a stainless steel spoon inside. It is then subjected to thermal shock test by heating […]

Filed Under: Failure Analysis Tagged With: Borosilicate Glass, Glass Blender, Jar, Thermal Shock

  • « Previous Page
  • 1
  • …
  • 24
  • 25
  • 26
  • 27
  • 28
  • …
  • 61
  • Next Page »

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering