Glass Failure Analysis of Wine Bottle

May 29, 2017 By Tom Read Leave a Comment

Failure Analysis - Wine Bottle Bare Neck

California Glass Failure Expert performs failure analysis of wine bottle revealing a manufacturing defect. In this case, the root cause is a piece of unmelted glass.

Filed Under: White Papers Tagged With: Bottle, Failure, Glass

Glass Failure Analysis of Beer Bottle

May 28, 2017 By Tom Read Leave a Comment

Beer Bottle Failure Analys

California Glass Failure Expert performs analysis on an exploding beer bottle. Failure analysis demonstrates that previous damage caused the delayed failure.

Filed Under: White Papers Tagged With: Bottle, Failure, Glass

Glass Failure Analysis of Wine Bottle Fracture

April 12, 2017 By Tom Read Leave a Comment

Glass Failure Analysis of Wine Bottle Fracture

California Glass Failure Expert performs a root cause failure analysis of a broken wine bottle. Included is an analysis of damage caused by the cork screw, crack initiation and crack propagation.

Filed Under: White Papers Tagged With: Bottle, Glass, Wine Bottle

Glass Expert Performs a Failure Analysis on a Broken Wine Bottle

June 22, 2016 By Tom Read Leave a Comment

Read Consulting glass experts performed a failure analysis on a broken wine bottle. The failure analysis determined that the side of the cork screw had exited the cork and created glass damage that initiated a failure when the cork was being removed. The side of the cork screw crushed the interior wall of the bottle […]

Filed Under: Failure Analysis Tagged With: Bottle, Failure, Glass

Glass Bottle Failure Analysis

March 3, 2014 By Tom Read Leave a Comment

Larger Point Impact (1/8″ Dia.) Fracture Surface at Originof 1/8″ at 40X Small Point Impact (1/32″ Dia.) Fracture Surface at Originof 1/32″ at 40X Often bottles and other glass objects fail as a result of “point impact”. Given here are two examples of point impact failure origins discovered as a result of glass failure analysis […]

Filed Under: Failure Analysis Tagged With: Bottle, Glass

  • 1
  • 2
  • 3
  • …
  • 8
  • Next Page »

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering