Failure Analysis Expert Discusses Metal Fatigue

March 31, 2009 By Tom Read Leave a Comment

Failure analysis was performed on a failed pin from a large tractor. The upper right gives an overview of the pin. Upper left is a close up of the fracture surface. The fatigue crack originated at the top of the photo and progressed downward until the final overload failure.

 

 

Share this:

  • Facebook
  • LinkedIn
  • Twitter
  • Pinterest
  • Print

Filed Under: Failure Analysis Tagged With: Fatigue Crack, Metal Fatigue, Overload Failure, Tractor

Leave a Reply Cancel reply

Your email address will not be published. Required fields are marked *

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Subscribe to Articles & White Papers

Enter your email address to subscribe to this blog and receive notifications of new posts by email.

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2022 Read Consulting · Materials Failure Analysis And Process Engineering