Fracture Surface of Thermally Tempered Glass Fracture Surface of Chemically Tempered Glass The Glass Expert Witness at Read Consulting have performed hundreds of glass failure analysis on tempered glass pieces. These include both thermally tempered and chemically tempered glass. Thermally tempered glass has compressive stress on its surfaces. The thickness pf the compressive layer is a […]
Touch Screen Failure Analysis Failure Analysis of Chemically Tempered Glass
Fracture Surface of Chemically Tempered Glass Taken at the origin Mag 30 X The glass failure analysis experts at Read Consulting failure analysis labs have over 40 years of experience working with chemically tempered glass (such as gorilla glass). Chemical tempering uses ion exchange techniques to create surface compressive stresses. Unlike thermally tempered glass, the thickness […]
Tempered Glass Oven Door Thermal Shock Test Failures
Glass experts at Read Consulting performed a glass failure analysis on several fully tempered glass oven doors that failed in an unexpected manner during thermal shock testing. 100% of these doors failed the glass thermal shock test. The subject tempered glass doors were painted with a 20µ thick picture frame on one side (top left […]
California Window Expert Performs Tempered Glass Failure Analysis
California glass expert was asked to perform a glass failure analysis on a glass door that failed spontaneously, The failure analysis lab located the failure origin. The glass experts then examined the fracture surface at the origin, and they determined that the root cause of the failure was a nickel sulfide particle. The failure origin magnified 200X […]
Tempered Glass Expert Performs Failure Analysis
California Failure Analysis Lab routinely performs tempered glass failure analysis. In this case the glass expert determined that the tempered glass failed as a result of a pointed object that created crush damage that penetrated the compressive layer of the tempered glass. The glass was a large piece 10 mm thick. Thus, the compressive layer […]