Glass Failure Analysis of Tempered Glass

April 8, 2017 By Tom Read Leave a Comment

Glass Failure Analysis of Tempered Glass

California Materials Failure Expert performs a Root Cause failure analysis of two tempered glass objects; a basketball backboard and a pickup truck rear window. Includes a discussion of Polarimeter surface stress measurements using a Strainoptics Grazing Angle Surface Polarimeter, GASP. Included is a detailed glass fracture analysis which includes determining the failure origin. This failure analysis study demonstrates how to analyze tempered glass.

 

Filed Under: White Papers Tagged With: Glass, Glass Fracture, Tempered Glass

Glass Expert Performs a Failure Analysis on a Broken Wine Bottle

June 22, 2016 By Tom Read Leave a Comment

Read Consulting glass experts performed a failure analysis on a broken wine bottle. The failure analysis determined that the side of the cork screw had exited the cork and created glass damage that initiated a failure when the cork was being removed. The side of the cork screw crushed the interior wall of the bottle […]

Filed Under: Failure Analysis Tagged With: Bottle, Failure, Glass

Failure Analysis of Restaurant Glass Coffee Mug

February 1, 2015 By Tom Read Leave a Comment

Failure analysis laboratory performed a root cause failure analysis on a restaurant glass coffee mug that failed unexpectedly when it was lifted off the table and injured a server. The bottom of the mug separated from the rest of the mug . The origin of the failure was on the interior of the mug at […]

Filed Under: Failure Analysis Tagged With: Coffee Mug, Glass, Mug

Glass Expert performs a Failure Analysis of a Wine Glass

November 9, 2014 By Tom Read Leave a Comment

 California glass expert performed a failure analysis on a failed wine glass. Glass failure analysis requires locating the fracture origin. The origin is then analyzed microscopically to determine the cause of failure. In this case the failure origin was on the rim of the glass. At the failure origin is a very small mirror fracture […]

Filed Under: Failure Analysis Tagged With: Glass, Wine, Wine Glass

Glass Bowl Failure Analysis

July 17, 2014 By Tom Read Leave a Comment

A Read Consulting glass expert witness performed a glass failure analysis of a glass crack driven by thermal stresses. The failed bowl cracked in a microwave oven. Often failures with known causes can be analyzed to lend insight as to the cause of an “unknown” glass fracture. This fracture has many of the aspects of […]

Filed Under: Failure Analysis Tagged With: Bowl, Glass

  • « Previous Page
  • 1
  • 2
  • 3
  • 4
  • …
  • 19
  • Next Page »

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering