Array of Pogo Pins Top of Pogo Pin at Mag. 30 X Cross sectioned Pogo Pins at Mag. 5 X Read Consulting Failure Analysis Labs often perform electronic failure analysis for various manufacturers. The objective is to determine the root cause of the failure and help the manufacturer correct the problem.In this case, a company […]
Read Consulting Failure Analysis Blog
In addition, READ CONSULTING provides services to industry in the areas of failure analysis, process development and process improvement. Read Consulting is prepared to use its experience and expertise to analyze customers' specific problems.
Tempered Glass Expert Discusses Tempered Glass Fracture Surfaces
Fracture Surface of Thermally Tempered Glass Fracture Surface of Chemically Tempered Glass The Glass Expert Witness at Read Consulting have performed hundreds of glass failure analysis on tempered glass pieces. These include both thermally tempered and chemically tempered glass. Thermally tempered glass has compressive stress on its surfaces. The thickness pf the compressive layer is a […]
Touch Screen Failure Analysis Failure Analysis of Chemically Tempered Glass
Fracture Surface of Chemically Tempered Glass Taken at the origin Mag 30 X The glass failure analysis experts at Read Consulting failure analysis labs have over 40 years of experience working with chemically tempered glass (such as gorilla glass). Chemical tempering uses ion exchange techniques to create surface compressive stresses. Unlike thermally tempered glass, the thickness […]
Surgical Screw Failure Analysis, Metal Fatigue
Read Consulting performed a metal failure analysis on two surgical screws that were used to hold wire for a surgical implanted back support system. These titanium screws failed after less than one year after the surgical implant.The failure analysis determined that both screws failed at the minor diameter due to metal fatigue in bending. […]
Diamond Tool Design{ Glass Expert Discusses Glass Damage From Diamond Grinding
Chart Showing Damage Depth of Diamond Grind v. Diamond Particle Size Checks in Glass Revealed by Etching with Buffered HF 100 Grit Damage Remaining After 0.0075″ Had Been Removed Certain types of glass must be ground to shape with a diamond tool, and they are then lapped and polished to make them transparent. If this […]