Shot Glass Failure Analysis

February 3, 2013 By Tom Read Leave a Comment

The glass expert at Read Consulting failure analysis lab was asked to perform a failure analysis on a glass sliver removed from a woman’s stomach. The woman had been out drinking the night before, and the following morning had stomach pains. The cause of the pain was found to be a glass sliver logged in her stomach. Part of the analysis […]

Filed Under: Failure Analysis Tagged With: Glass, Shot Glass

California Glass Expert Examines an Aircraft Windshield Failure

January 26, 2013 By Tom Read Leave a Comment

Read Consulting failure analysis lab performed a glass failure analysis on a failed aircraft windshield. The  windshield of a turbo-prop aircraft suddenly cracked during descent through clouds. Initially it was thought that static electricity had caused the glass failure. Initially it was proposed that the static electricity sought the aircraft “ground” through heating wires in […]

Filed Under: Failure Analysis Tagged With: Aircraft Windshield, Conchoidal Fracture

Food Contamination: Wine Bottle Contaminant

January 6, 2013 By Tom Read Leave a Comment

 Although Read consulting is a failure analysis lab, Failure experts at Read Consulting have worked with numerous food packaging companies to determine the cause of food contamination and work with food packaging companies to correct the problems they are encountering. In this case, a claim was made that a mobile wine bottling line was damaging […]

Filed Under: Failure Analysis Tagged With: Bottle, Contaminant, Glass, Wine Bottle

Failure Analysis of Glass Encapsulated Zener Diodes

December 22, 2012 By Tom Read 2 Comments

Failure Analysis Lab examines performs a failure analysis on surface mount glass encapsulated Zener diodes. These diodes were in an appliance control board, and they are surface mounted to the underside a printed circuit board. The entire board is encapsulated in rigid polyurethane. There was a significant yield loss due to cracking of the glass […]

Filed Under: Failure Analysis Tagged With: Encapsulated Zener Diodes, Glass

Glass Expert Performs Failure Analy on Low E Windows

December 1, 2012 By Tom Read Leave a Comment

California failure analysis lab was asked to determine why windows in an expensive hilltop home failed. The windows in question were Lo- E windows that were tinted to absorb infra-red light. At this location two south facing, side-by-side windows cracked. The window expert at Read Consulting was asked to perform a glass failure analysis to […]

Filed Under: Failure Analysis Tagged With: Glass, Low E Windows, Window

  • « Previous Page
  • 1
  • …
  • 26
  • 27
  • 28
  • 29
  • 30
  • …
  • 61
  • Next Page »

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering