Glass Expert at Read Consulting is asked to assess whether a broken window or shower door was fully tempered. One method is to select the ten largest “crack free” pieces and determine if these can fit into a 10 square inch area. In the photo above, a 3″ X 3″ (approximately 10 square inches) “frame” […]
Tempered Glass Failure: Nickel Sulfide Particle
California failure analysis expert examines glass door failure to determine the root cause of the failure. The subject tempered glass door failed spontaneously, and because the glass was verticle, the broken pane remained intact. Read Consulting failure analysis laboratory was able to obtain the origin and perform a root cause failure analysis. The attached 25X Nomarski photomicrograph […]
Glass Failure Expert Looks at Tempered Glass Failure
Glass expert analyzed a broken tempered glass door. He was able to preserve the origin and perform a failure analysis. The spontaneous glass failure started in the center of the window and was caused by a nickel sulfide particle (NiS particle). This failure mechanism is well known and has been documented by others. In this […]