Even though glass is a brittle material, there are times that a crack can stop and later re-start. Above is a photo micro graph of the region around crack origin in borosilicate glass. Two apparent crack arrest lines are indicated. There are more near the origin. These indicate that after originating, this crack stop several times before complete failure.