California Glass Expert Examines an Aircraft Windshield Failure

January 26, 2013 By Tom Read Leave a Comment

Read Consulting failure analysis lab performed a glass failure analysis on a failed aircraft windshield. The  windshield of a turbo-prop aircraft suddenly cracked during descent through clouds. Initially it was thought that static electricity had caused the glass failure. Initially it was proposed that the static electricity sought the aircraft “ground” through heating wires in […]

Filed Under: Failure Analysis Tagged With: Aircraft Windshield, Conchoidal Fracture

Food Contamination: Wine Bottle Contaminant

January 6, 2013 By Tom Read Leave a Comment

 Although Read consulting is a failure analysis lab, Failure experts at Read Consulting have worked with numerous food packaging companies to determine the cause of food contamination and work with food packaging companies to correct the problems they are encountering. In this case, a claim was made that a mobile wine bottling line was damaging […]

Filed Under: Failure Analysis Tagged With: Bottle, Contaminant, Glass, Wine Bottle

Failure Analysis of Glass Encapsulated Zener Diodes

December 22, 2012 By Tom Read 2 Comments

Failure Analysis Lab examines performs a failure analysis on surface mount glass encapsulated Zener diodes. These diodes were in an appliance control board, and they are surface mounted to the underside a printed circuit board. The entire board is encapsulated in rigid polyurethane. There was a significant yield loss due to cracking of the glass […]

Filed Under: Failure Analysis Tagged With: Encapsulated Zener Diodes, Glass

Glass Expert Performs Failure Analy on Low E Windows

December 1, 2012 By Tom Read Leave a Comment

California failure analysis lab was asked to determine why windows in an expensive hilltop home failed. The windows in question were Lo- E windows that were tinted to absorb infra-red light. At this location two south facing, side-by-side windows cracked. The window expert at Read Consulting was asked to perform a glass failure analysis to […]

Filed Under: Failure Analysis Tagged With: Glass, Low E Windows, Window

Tempered Glass Expert Performs Failure Analysis

November 18, 2012 By Tom Read Leave a Comment

California Failure Analysis Lab routinely performs tempered glass failure analysis. In this case the glass expert determined that the tempered glass failed as a result of a pointed object that created crush damage that penetrated the compressive layer of the tempered glass. The glass was a large piece  10 mm thick. Thus, the compressive layer […]

Filed Under: Failure Analysis Tagged With: Tempered Glass

  • « Previous Page
  • 1
  • …
  • 26
  • 27
  • 28
  • 29
  • 30
  • …
  • 61
  • Next Page »

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering