Glass Cookware Failure Analysis: Pyrex Pie Plate Failure

February 18, 2014 By Tom Read Leave a Comment

Fracture Surface at One Failure Origin Assembled Pie Plate Showing Several Failure Origins Read Consulting Failure analysis lab performed a glass failure analysis. An annealed borosilicate glass Pyrex baking dish failed as a result “thermal shock”. There were multiple origins for the failure, and these all initiated at damage sites on the bottom of the […]

Filed Under: Failure Analysis Tagged With: Bottle, Cookware, Glass, Pyrex

Window Defect Analysis Capabilities

February 10, 2014 By Tom Read Leave a Comment

Reflected Zebra Board Image that Shows Window Roller Distortion Created During The Thermal Temper Process Window Scratches Caused by PoorCleaning Procedures The window experts at Read Consulting are often asked to evaluate windows for defects. Many of these are Low-E windows that are also tempered. Two typical defects found are scratches and roller distortion.Often the scratches […]

Filed Under: Failure Analysis Tagged With: Distortion, Low-E, Roller Distortion, Scratching, Tempered Glass, Window Defect

Plastic Failure Analysis: Fusion Welded HDPE

February 3, 2014 By Tom Read Leave a Comment

Poor Welding of a CarrierPipe Joint There was no Melting on a part of the joint Read Consulting, a California failure analysis lab, has performed numerous plastic failure analysis on various types of plastic pipe. This includes PVC, CPVC, Delrin and Polypropylene. In this case a plastic failure analysis was performed on a failed containment waste […]

Filed Under: Failure Analysis Tagged With: CPVC, Fusion Welded HDPE, Plastic Failure, PVC

Storage Tank Failures, Tank Failure Analysis

January 15, 2014 By Tom Read Leave a Comment

Storage tanks have a finite lifetime, and they should be carefully inspected annually. Read Consulting has performed numerous storage tank failure analysis. Steel tank failures were caused by corrosion. PVC tanks failures were caused by UV degradation of the polymer. Attached are two representative photos of tank failures analyzed in the past. One failure was […]

Filed Under: Failure Analysis Tagged With: Corrosion, PVC, Storage Tank, UV Degradation

Failure Analysis Lab Analyzes Shower Door Failure

December 15, 2013 By Tom Read Leave a Comment

Installed Shower Door   Top Roller  at Stop Disassembled Roller   Fracture Surface at Origin Tempered glass shower doors have been modernized. Recent designs have the doors suspended by rollers that ride on a pipe. In certain cases the door stop is on the top. In this case, the roller is stopped by a rubber […]

Filed Under: Failure Analysis Tagged With: Glass, Shower Door Failure, Tempered Glass

  • « Previous Page
  • 1
  • …
  • 22
  • 23
  • 24
  • 25
  • 26
  • …
  • 61
  • Next Page »

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

  • Home
  • About
  • Experience
  • Expertise
  • Laboratory
  • Failure Analysis
  • Blog
  • White Papers

Read Consulting Failure Analysis

Thomas L. Read, PhD,
1435 Fulton Road Santa Rosa, CA
Phone: 707-494-5089
email: info@readconsulting.com

Connect With Read Consulting

FacebookTwitterLinkedinYouTubeRSS Feed

Registered Professional Engineer

Thomas L. Read, PhD., CEO
Registered Professional Engineer
Certificate No. MF002174
State of California.

Copyright © 2025 Read Consulting · Materials Failure Analysis And Process Engineering